Tus ua plaub0Cr15al5Alloy Kuj Sawb los ntawm Lub Hoobkas
Teem nqi | 0Cr15al5 |
Qhov loj | Thickness: 0.05-3mm Dav: 4-250mm |
Nplaim | Ci ntsa iab |
Qho hnyav | 5-200kg / yob, raws li cov neeg siv khoom siv |
Resiveivity | 1.3 ± 0.05μω.m |
Hardness (HV) | 180-210hv |
Elongation | ≥16% |
Teem nqi | Siab tshaj plaws kub | Resiveivity | Kev nyuaj | Lub zog tensile | Elongation |
0C13Al4 | 1050 ℃ | 1.25 ± 0.05μω.m | 180-210hv | ≥550n / mm2 | ≥16 |
0Cr15al5 | 1100 ℃ | 1.3 ± 0.05μω.m | 180-210hv | ≥550n / mm2 | ≥16 |
0cr21al6nbb | 1300 ℃ | 1.42 ± 0.05μω.m | 200-240hv | 750n / mm2 | ≥12 |
Cr20NI80 | 1200 ℃ | 1.09 ± 0.05μω.m | 180-220hv | 750n / mm2 | ≥20 |
Cr15ni60 | 1150 ℃ | 1.12 ± 0.05μ.m | 175-210hv | 750n / mm2 | ≥20 |
Cr20ni35 | 1100 ℃ | 1.04 ± 0.05μω.m | 180-220hv | 750n / mm2 | ≥20 |
Cr25ni20 | 1100 ℃ | 0.86 ± 0.05μω.m | 180-220hv | 750n / mm2 | ≥20 |
Teem nqi | Tshuaj Yeeb Nkab% | ||||||||
C | P | S | Mn | Si | Cr | Ni | Al | Fe | |
≤ | |||||||||
0Cr15al5 | 0.04 | 0.02 | 0.01 | 0.3 | I≤0.5 | 13-14 | <1 | 4.8-5.0 | seem |
0cr21al6nbb | 0.05 | 0.025 | 0.02 | 0.5 | I≤0.6 | 21-23 | I≤0.6 | 5-7 | seem |
0C13Al4 | 0.04 | 0.02 | 0.01 | 0.3 | I≤0.5 | 13-14 | <1 | 4.8-5.0 | seem |
Cr20NI80 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 20-23 | seem | <0.5 | I≤1.0 |
Cr15ni60 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 15-18 | 55-61 | <0.5 | seem |
Cr20ni35 | 0.08 | 0.02 | 0.015 | 1.0 | 1-3 | 18-21 | 34-37 | - | seem |
Cr25ni20 | 0.08 | 0.045 | 0.03 | 2.0 | 0.4-0.6 | 24-26 | 19-22 | - | seem |
Shanghai Tankii Alloy Khoom Co., Ltd. Tsom xam rau kev tsim khoom ntawm nichrome alloy, cermocouple xaim, tooj liab alloy, tooj liab alloy, tooj liab, xev, sawb, pas nrig, pas nrig.
Peb twb tau txais ISO 9001 daim ntawv pov thawj zoo thiab kev pom zoo ntawm ISO ntau lawm tsim, kev kho mob thiab kho kom kub ntxhov.