Tuam Tshoj Feni Nickel Hlau Alloy Precision 0.5mm Invar 35MM rau sealing precision ntsuas khoom thiab Hoobkas Tankii

Feni Nickel Hlau Alloy Precision 0.5mm Invar 36 Hlau rau Sealing precision ntsuas

Cov lus piav qhia luv luv:

Qauv NO.:Lus hauv 36 Hlau

Khoom siv:Fe- ni alloy

Nto:Du thiab ci

Mob:Mos, 1 / 2h. Tawv

Inch:0.02- 5.0mm

HS code:75125000

Ntom ntom (G / cm3):8.1

Xa email rau peb

Khoom Qhia Qhia

Cov FAQ

Khoom Ntawv

Feni Nickel Hlau Alloy Precision 0.5mmLus hauv 36 HlauRau sealing precision ntsuas

Caw 36yog npib tsib xee-hlau, tsis muaj expansion alloy muaj 36% npib tsib xee. Nws tau tswj hwm ze li qhov ntau ntawm cov kev siv hluav taws xob ib txwm muaj, thiab muaj qhov tsis tshua muaj zog ntawm kev siv lub zog zoo thiab muaj zog ntawm cov tshuab ntxhua khaub ncaws cryogenic zoo.

Caw 36tuaj yeem ua tau kub thiab txias tsim thiab machined siv cov txheej txheem zoo ib yam li

Austenitic stainless hlau. Invar 36 yog weldable siv cev cov tub lim hlau CF36 uas yog

Muaj nyob rau hauv liab qab xaim rau ob qho tib si gtaw thiab GMAW txheej txheem.

Tshuaj Muaj Tshuaj

muaj pes tsawg	%	Fe	Ni	Mn	C	P	S	SI
zoo siab	lub min	Tus liab	35.0	0.2
zoo siab	tus zuag	Tus liab	37.0	0.6	0.05	0.02	0.02	0.3

Cov Khoom Siv Lub Cev

Ntom ntom (G / cm3) 8.1

Hluav taws xob tiv thaiv hluav taws xob ntawm 20ºC (mm2 / Txiv neej) 0.78

Factor ntawm resistivity (20ºC ~ 200ºC) x10-6 / ºC 3.7 ~ 3.9

Thermal conductivity, λ / w / (m * ºC) 11

Curie taw tes TC / ºC 230

Elastic modulus, E / GPA 144

Melting Taw tes ºC 1430

Coefficient ntawm expansion

θ / ºC	α1 / 10-6ºC-1	θ / ºC	α1 / 10-6ºC-1
20 ~ -60	1.8	20 ~ 250	3.6
20 ~ -40	1.8	20 ~ 300	5.2
20 ~ -20	1.6	20 ~ 350	6.5
20 ~ -0	1.6	20 ~ 400	7.8
20 ~ 50	1.1	20 ~ 450	8.9
20 ~ 100	1.4	20 ~ 500	9.7
20 ~ 150	1.9	20 ~ 550	10.4
20 ~ 200	2.5	20 ~ 600	11.0

Raug Cov Khoom Siv Neeg Kho Tshuab

Lub zog tensile	Elongation
MPa	%
641	14
689	9
731	8

Qhov Kub NtawmRqhov tseem ceeb

Qhov kub thiab txias, ºC	20 ~ 50	20 ~ 100	20 ~ 200	20 ~ 300	20 ~ 400
AR / 103 * ºC	1.8	1.7	1.4	1.2	1.0

Cov txheej txheem kho cua sov
Annealing rau Kev Nyuaj Siab nyem	Rhuab rau 530 ~ 550ºC thiab tuav 1 ~ 2 h. Txias
ib tug anerting	Txhawm rau tshem tawm cov tawv tawv tawv, uas yuav coj tawm hauv cov txheej txheem txias, cov txheej txheem kos txias. Annealing xav tau rhuab rau 830 ~ 880ºC hauv lub tshuab nqus tsev, tuav 30 min.
Txheej txheem stabilization	Hauv kev tiv thaiv media thiab rhuab rau 830 ºC, tuav 20min. ~ 1h, quench Vim yog cov kev ntxhov siab tsim los ntawm quenching, rhuab rau 315ºC, tuav 1 ~ 4h.
Cov kev ceev faj	Tsis tuaj yeem ua kom tawv tawv los ntawm kev kho cua sov Cov kev kho deg tuaj yeem yog sandblasting, polishing lossis pickling. Alloy tuaj yeem siv 25% hydrochloric acid pickling tov ntawm 70 ºC kom meej meej oxidized nto