Ferrroalloys OCR21AL6 0.14mm Kuj Hlau Hlau Rau Khoom Siv Hluav Taws Xob
Ferrroalloys OCR21AL6 0.14mm Kuj Hlau Hlau Rau Khoom Siv Hluav Taws Xob
| Teem nqi | 0CR21AL6 |
| Qhov loj | 0.14mm |
| Nplaim | Ci Ntsej Muag |
| Qho hnyav | 0.64kg / yob |
| Resiveivity | 1.45 ± 0.07μ.m |
| Siab tshaj plaws kub | 1350 ℃ |
| Ceev | 7.1g / cm³ |
| Lub zog tensile | 750n / mm² |
| Elongation | ≥12 |
| Teem nqi | Siab tshaj plaws kub | Resiveivity | Melting taw tes | Lub zog tensile | Elongation |
| 0cr214al4 | 1100 ℃ | 1.23 ± 0.06μμμμμμμμμω.m | 1500 ℃ | 750 | ≥12 |
| 0CR25AL5 | 1250 ℃ | 1.42 ± 0.07μ.m | 1500 ℃ | 750 | ≥12 |
| 0cr23al5 | 1300 ℃ | 1.35 ± 0.06μμμμμμμμμμμμμμω.m | 1500 ℃ | 750 | ≥12 |
| 0cr2 2012nbco | 1350 ℃ | 1.45 ± 0.07μ.m | 1510 ℃ | 750 | ≥12 |
| 0cr27al7mo2 | 1400 ℃ | 1.53 ± 0.07μ.m | 1520 ℃ | 750 | ≥10 |
| Ksc | 1350 ℃ | 1.44 ± 0.05μω.m | 1510 ℃ | 750 | ≥16 |
| Cr20NI80 | 1200 ℃ | 1.09 ± 0.05μω.m | 1400 ℃ | 750 | ≥20 |
| Cr15ni60 | 1150 ℃ | 1.12 ± 0.05μ.m | 1390 ℃ | 750 | ≥20 |
| Cr20ni35 | 1100 ℃ | 1.04 ± 0.05μω.m | 1390 ℃ | 750 | ≥20 |
| Cr20NI30 | 1100 ℃ | 1.04 ± 0.05μω.m | 1390 ℃ | 750 | ≥20 |
| Teem nqi | Tshuaj Yeeb Nkab% | ||||||||
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | |
| ≤ | |||||||||
| 0cr214al4 | 0.12 | 0.025 | 0.025 | 0.7 | I≤1.0 | 17-21 | I≤0.6 | 3-4 | seem |
| 0CR25AL5 | 0.06 | 0.025 | 0.02 | 0.5 | I≤0.6 | 23-26 | I≤0.6 | 4.5-6.5 | seem |
| 0cr23al5 | 0.06 | 0.025 | 0.02 | 0.5 | I≤0.6 | 20.5-23.5 | I≤0.6 | 4.2-5.3 | seem |
| 0cr21al6nbb | 0.05 | 0.025 | 0.02 | 0.5 | I≤0.6 | 21-23 | I≤0.6 | 5-7 | seem |
| 0cr27al7mo2 | 0.05 | 0.025 | 0.02 | 0.2 | I≤0.4 | 26.5-27.8 | I≤0.6 | 6-7 | seem |
| Cr20NI80 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 20-23 | seem | <0.5 | I≤1.0 |
| Cr15ni60 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 15-18 | 55-61 | <0.5 | seem |
| Cr20ni35 | 0.08 | 0.02 | 0.015 | 1.0 | 1-3 | 18-21 | 34-37 | - | seem |
| Cr20NI30 | 0.08 | 0.02 | 0.015 | 1.0 | 1-3 | 18-21 | 30-34 | - | seem |