Lub leeg | C≤ | PC | S≤ | Mn | Si | Cu≤ | Mo | Ni | Zaum fe |
Muaj pes muaj% | 0.03 | 0.02 | 0.02 | 0.6-1.1 | 0.3-0.5 | 0.20 | 3..1-4.1 | 78.5-80.0 | Qho tseg |
Sau ntawv:
Cov duab thiab qhov loj me ntawm cov alloys tau ua raws li GBN198-88
Rooj 2 Lub cev yuav tsum tau ua
Ntiag tug | Resisitivity (μωm) | Desinty (g / cm3) | Curie point.c | Lub Siab Muaj Zog Magneto-Tawv Coeffentλientθ / 10-6 |
Tus nqi | 0.55 | 8.6 | 450 | 2 |
Rooj 3 AC Cov Khoom Sib Nqus Sib Nqus Rau Cov Sawb (Min Tus Nqi)
Qhov tuab | Lub ncov rau lub zog sib nqus lub zog yog 0.1a / m, nyob rau hauv txawv tas li offlexible priceability μm / (mH / m) | |||
60HZ | 400Hz | 1kHz | 10KHZ | |
0.02 | 17.5 | 12.5 | ||
0.05 | 18.8 | 9.4 | ||
0.10 | 22.5 | 15 | ||
0.20 | 12.5 | 7.5 | ||
0.35 | 25 | 8.8 |
Cov lus 4 coefficient ntawm linear nthuav dav ntawm qhov kub hloov / (x10-6)
Temp | 20-100 ° C | 20-200ºC | 20-300ºC | 20-400ºC | 20-500ºC | 20-600ºC | 20-700ºC |
Tus nqi | 1.3-10.8 | 10.9-11.2 | 14.4-12.9 | 11.9-12.5 | 12.3-13.2 | 12.7-13.4 | 13.1-13-13.6 |
Rooj 5 Sib Nqus Yuav Tsum (Muab Qhuav Rolling Sawb)
Qib Kuv
(Δ & d) / hli | μ0.08 / (MHM) ≥ | μm (MHM) ≥ | BS / T≥ | HC (A / M) ≤ |
0.005 | 12.5 | 44.0 | 0.75 | 6.4 |
0.01 | 17.5 | 87.5 | 0.75 | 4.8 |
0.02-0.04 | 20.0 | 112.5 | 0.75 | 4.0 |
0.05-0.09 | 22.5 | 137.5 | 0.75 | 2.8 |
0.10-0.19 | 25.0 | 162.5 | 0.75 | 2.0 |
0.20-0.34 | 28.0 | 225.0 | 0.75 | 1.6 |
0.35-1.00 | 30.0 | 250.0 | 0.75 | 1.2 |
1.10-2.50 | 27.5 | 225.0 | 0.75 | 1.6 |
2.50-3.00 | 26.3 | 187.5 | 0.75 | 2.0 |
Qib II
(Δ & d) / hli | μ0.08 / (MHM) ≥ | μm (MHM) ≥ | BS / T≥ | HC (A / M) ≤ |
0.02-0.04 | 22.5 | 125.0 | 0.75 | 2.4 |
0.05-0.09 | 25.0 | 150.0 | 0.75 | 2.0 |
0.10-0.19 | 27.5 | 187.5 | 0.75 | 1.6 |
0.20-0.34 | 31.3 | 250.0 | 0.75 | 1.2 |
0.35 | 32.5 | 275.0 | 0.75 | 0.79 |
Qib III
(Δ & d) / hli | μ0.08 / (MHM) ≥ | μm (MHM) ≥ | BS / T≥ | HC (A / M) ≤ |
0.01 | 25.0 | 150.0 | 0.73 | 2.4 |
0.02-0.04 | 31.0 | 190 | 0.73 | 1.6 |
0.05-0.09 | 38.0 | 250.0 | 0.73 | 1.2 |
0.10-0.19 | 38.0 | 250.0 | 0.73 | 1.2 |
0.20-0.34 | 38.0 | 280.0 | 0.73 | 1.0 |
0.35 | 44.0 | 310.0 | 0.73 | 1.0 |
Kub Rolling (Forging) Flastspring
(Δ & d) / hli | μ0.08 / (MHM) ≥ | μm (MHM) ≥ | BS / T≥ | HC (A / M) ≤ |
3-22 | 25.0 | 125 | 0.75 | 2.4 |
Kub Rolling (Forging) Bar
(Δ & d) / hli | μ0.08 / (MHM) ≥ | μm (MHM) ≥ | BS / T≥ | HC (A / M) ≤ |
8-100 | 25.0 | 125.0 | 0.75 | 2.4 |